Product Details:
|
| Application: | Bearings Mechanical Seals Bearings Valve Plates Ball Valves Nozzles Pipeline Lining Thermocouple Protection Tube | Material: | Al2O3 Aluminum Oxide, 95%, 99% |
|---|---|---|---|
| Color: | White | Size: | Customized |
| Shape: | Round, Balls, Irregular, Tube, Customized | Density: | >=3.6g / Cm3 |
| Feature: | Wear Resistant Corrosion Resistant Thermal Shock Resistant High Strength Air Impermeability | Product Name: | Manufacturer Supplier 95%-99.8% Aluminum Oxide Ceramic Al2O3 Crucibles, Alumina Furnace Tube, Al2O3 Grinding Polishing Packing Ceramic Balls, Alibaba China Wear-resisting Alumina Ceramics, Al2O3 Aluminium Oxide Alumina Ceramic |
| High Light: | 230MPa Aluminum Oxide Ceramics,230MPa Setter kiln furniture,99% Al2O3 kiln furniture |
||
Setter / kiln furniture used for
sintering and debinding metal injection moulded (MIM) components
In the metal powder injection molding (MIM) industry for many years accumulated rich experience, for our products in the application of customers to win wide recognition! According to customers' different sintering degreasing process and customer's product requirements, provide the best ceramic sintering carrier.
Advantage:
Ceramic sintering carrier for continuous furnace
LM-Z868, Using high-purity raw materials, the product has a good surface finish. It is mainly used for continuous furnace sintering of stainless steel 304, 316 and iron-based materials. The ceramic plate has a long service life. Does not react with sintered products.
Specification:
Al2O3 % ≥90
SiO2 % ≤10
Fe2O3 % ≤0.1
Na2O3 % ≤0.1
Mgo % ≤0.1
Bulk density: 2.9 g/cm2
Apparent porosity 20%
Bending Strength 230MPa
Coefficient of thermal expansion 7.0 A×10-6/℃
Working Temp. ≤1650℃
LM-900 Advanced process formula, high purity raw materials. The surface is smooth, flat, high precision size control, high temperature resistance, long-term use without deformation.It is suitable for sintering stainless steel 304, 316 and tungsten alloy in continuous furnace at 1500 ℃
Specification:
Al2O3 % ≥95
SiO2 % ≤5
Fe2O3 % ≤0.1
Na2O3 % ≤0.05
Mgo % ≤0.05
Bulk density: 2.9 g/cm2
Apparent porosity 19%
Bending Strength 240MPa
Coefficient of thermal expansion 7.0 A×10-6/℃
Working Temp. ≤1650℃