Product Details:
|
| Shape: | Round, Square, Rectangular Or Other Customized Shapes | Application: | Si3N4 Forming Rollers |
|---|---|---|---|
| Density: | 3.22g/cm3 | Material: | Silicon Nitride |
| High Light: | Si3N4 Nozzle Silicon Nitride Ceramics,Oxidation Resistance Silicon Nitride Ceramics,High Toughness Silicon Nitride Ceramics |
||
Silicon nitride nozzles and covers have the characteristics of oxidation resistance, high temperature strength and less sputter adhesion, which can prolong the service life of the welding parts.
In the five methods of silicon nitride production, GPSN is most commonly used to produce Si3N4 components. Here we introduce Gas pressure sintering (GPS):
Gas pressure sintering of silicon nitride is performed at a pressure of 1 to 10 MPa at a temperature of about 2000 ° C. The high nitrogen pressure suppresses the pyrolysis of silicon nitride. Due to the use of high-temperature sintering, it is sufficient to promote Si3N4 grain growth with the addition of less sintering aids, and obtain high-toughness ceramics with long columnar grains in situ growth density of> 99%. High toughness, high strength and good abrasion resistance can directly produce various complex shaped products close to the final shape, which can greatly reduce production costs and processing costs.
| Size | Customized |
| Color | Black |
| Density | 3.22 g/cm3 |
| Flexural strength | 800 MPa |
| Fracture toughness | 6.5 MPa m^1/2 |
| Thermal stress parameters | 569 K |
| Item | Unit | Si3N4 |
| Type | – | Gas pressure sintered |
| Density | g/cm3 | 3.22 |
| Color | – | dark grey |
| Water Absorption | % | 0 |
| Young Modulus | Gpa | 290 |
| Vickers Hardness | Gpa | 18 – 20 |
| Compressive Strength | Mpa | 2200 |
| Flexural Strength | Mpa | 650 |
| Thermal Conductivity | W/m.K | 25 |
| Thermal Shock Resistance | Δ(°C) | 450 – 650 |
| Max. Working Temp. | °C | 1200 |
| Volume Resistivity | Ω ·cm | > 10^14 |
| Dielectric Constant | – | 8.20 |
| Dielectric Strength | kV/mm | 16 |
| * Tests under room temperature environment;
* The above information is offered for comparison only. Exact properties will vary depending on the manufacturing method. |
||
-High strength over a wide temperature range
-High fracture toughness
-High hardness
-Outstanding wear resistance
-Low thermal expansion and high thermal conductivity
-Good thermal shock resistance
-Good resistance to chemical and oxidation
Send inquires to sales@industrial-ceramicparts.com for more information or any questions.
As a ceramic material, silicon nitride is quite fragile in a lot of cases. Our silicon nitride nozzle and covers are carefully handled to minimize damage during storage and transportation. Suitable outer boxes and inner cushioning materials are used for Si3N4products, vacuum packing is also engaged for some of the parts.